Lost Foam Casting Servo Motor Bracket

Рет қаралды 3,088

2 ай бұрын

Heading out to the casting shop today and start Manufacturing a servo motor adapter for an indexing fixture. First, we make the part out of foam then bury it in sand and lost foam and cast it. We don't get it on the first try and find casting defects but we learn lots on the way and in the end we nail it and cast a perfect part.
lots to learn on the way.

Пікірлер: 16

@Dellpodder 2 ай бұрын

Very cool to see this casting process done for functional parts. I'm looking forward to seeing the machining and installation!

@Wrighmachining 2 ай бұрын

Thank you jardamuth ! Should be next out march 15 for the machining video

@eyuptony 2 ай бұрын

That was excellent. Great result. Enjoyed watching. Cheers Tony

@Wrighmachining 2 ай бұрын

Tganks tony , glad you enjoyed it

@johnkoury1116 2 ай бұрын

That is so cool!! I am about to start building a gingery style milling machine with lost foam casting...Super cool!!!!

@Wrighmachining 2 ай бұрын

Awsome !! Should be a fun project . Keep me posted i would love to see the progress as you work your way through it. If youbhave any queations also im here to help of you need .

@johnkoury1116 2 ай бұрын

@@Wrighmachining I will definitely keep you informed. Thank you so much!

@johnkoury1116 2 ай бұрын

@@Wrighmachining I ordered a graphite crucible but when it got here it was much smaller than I had thought. I am going to use a cast iron stew pot instead. What do you think about using the cast iron pot?

@procyonia3654 2 ай бұрын

Alright this is some cool work brother

@Wrighmachining 2 ай бұрын

Thanks pro , Stoked for machining it this week and fitting it up

@KF-qj2rn Ай бұрын

any use of those low temp (gas torch) aluminum fill sticks (from harbor freight here) - "Weld aluminum with any low temperature torch - even a propane torch. These aluminum welding rods are harder than mild steel which results in minimized parent material distortion during welding. You’ll also get a stronger weld than the parent aluminum material without flux or other welding material. Harder than mild steel Low working temperature (730° F) No flux or fumes Excellent corrosion resistance Minimize parent material distortion during welding"

@Wrighmachining Ай бұрын

Yes , welding it had crossed my mind . I also have a alu welder ,but curiouse about the alu welding rodsa . Maby one day ill grab some and play with it . Could have been a viable way . Im glad i redid it though and didnt have to machine the ⅛ gap after casting .