It seems to me the key to getting it to work as well as it did was to allow the canister to forge weld to the exteriors of the ball bearing billet. Putting Ti02 inside the can would have prevented it from adhering to the canister and made the task of welding the balls together without filler material a wonky mess.

My thoughts exactly.... In the first 10second of the video i was shock

@brink666 my thoughts exactly and came to say the same exact thing. You can not get that pattern weld without 2 different types of metals so there is no way in this world he made the pattern look like that without a 2nd type of metal which the one he had forged out looked good so why fake the ending have no idea. Also I was shocked to see the first pass on the can he sqeezed down from the top really hard to where it almost blew it out and never seen that one before but good on him if it worked just wonder where he got the metal to make the blade bc I seen cpl patterns like that before on here by other smith's so wonder if he bought a bar for stock removal lol

​@HansKnives it's not ignorance you literally can't make a Damascus design with only 1 type of metal. If they are Nickle or whatever its still 1 type of steel and it would weld as a solid bar regardless of what ignorance your referring to it can not it will not ever work without a 2nd type of steel/ metal ro separate the bearings. Seen this pattern at least 5 times on here and every single one but him used powdered steel and never one time did they ever squeeze it that hard from the top and tell you you can't do that but hey it's others ignorance right for calling out a fake video. He made a nice bar to begin with so why try and make ppl belive he actually made that steel

The guys got a mill, no challenge at all

Hey didint think I'd find you here

Did it work ?

That's a Lady.

@@kyrerymmukk7446 nope

Because the container is too long and is directly detached from the container, poor welding will occur because there are only steel balls in the container. My approach was more cumbersome. Each has its pros and cons, and there are different choices available in different situations.

@@HansKnives If you have access to a mill, this is the only way to do it! Grinding and/or cutting the can off is always a pain. @danielstellmon5330 Since there’s no powdered steel filling in the gaps, you’ve really gotta compress this all the way through or you’ll have nasty inclusions through the middle of the billet. Forge welding the can to the BBs is the only way I can see this working without powdered steel, so a sacrificial layer in between would be counterproductive.

Except Hans adds handles

The hydraulic press was made by me. Thank you for your support.

@@HansKnives Would you consider making a video showing the press and what you learned from doing it? Or if you followed a guide or schematic, could you point us to the right direction? I've been collecting a bunch of blueprints for it and weighing pros and cons of different designs - yours looks very well thought out!

Thank you ！bro

Also, milling the billet is so much easier than grinding it off like so many do!

it is very pretty, but not damascus. it's pattern welded.

Thanks for explaining @@louiscyfer6944