Material Science, Heat Treatment of Steel, Part 3
Рет қаралды 3,425
Күн бұрынTempering and quenching, surface hardening and thermochemical diffusion treatment.
00:00 - Introduction
00:35 -Tempering
02:09 - Hardening and tempering
04:34 - Surface hardening
06:04 - Flame hardening
06:43 - Induction hardeninig
07:47 - Thermomechamichal Diffusion treatment
08:37 - Case hardening
11:41 - Nitriding
13:03 - Outro
@massivolleyballer 3 жыл бұрын
Wie immer top. 🙏👍👌
@gurugord 2 жыл бұрын
Well done! Thank you once again. Sushi?
@mohammadhamedmellati3290 2 жыл бұрын
thanks🌹🌹🌹🌹🙏🏻
@WeltderWerkstoffe 2 жыл бұрын
you are welcome
@wesleyparraassuncao4807 3 жыл бұрын
Muito bom!
@ElxMargerin 2 жыл бұрын
@ 1:25 it is stated that tempering at 180-250°C increases touges significantly. @ 2:04 it is stated that this effect can only be observed at 400°C. Which one is right? Did i miss something?
@WeltderWerkstoffe 2 жыл бұрын
There is a difference between "hardening" (followed by tempering at 180-250°C) to reach max hardness with adjusted toughness and "hardening and tempering" (tempering at above 400°C) to reach max toughness and increased hardness and strength.
@ElxMargerin 2 жыл бұрын
@@WeltderWerkstoffe thanks for the explanation :)
@user-mf7li2eb1o 3 жыл бұрын
Bitte separaten englischen kanal
@WeltderWerkstoffe 3 жыл бұрын
Das ist erst einmal nicht angedacht. So finden auch meine Studenten, die sich mit der englischen Sprache zum Teil leichter tun als mit der deutschen die entsprechenden Videos aus Englisch ganz unkompliziert.
tec-science
Рет қаралды 4,6 М.
Nikita Zdradovskiy
Рет қаралды 4 МЛН
Matallurgy Data
Рет қаралды 330 М.
FISPECKT
Рет қаралды 145 М.
Thebox - о технике и гаджетах
Рет қаралды 112 М.