How to Weave Glass with Lisa Vogt

Рет қаралды 1,184

2 ай бұрын

In today's video I will show you how to do the "weaving" technique with glass! This can be a fun project to do on its own OR you can incorporate this into a different piece as an accent. The possibilities can be endless!
I hope this inspires you to have a go at this fun and simple technique,
Happy Fusing!
Check out my website for an abundance of FREE fusing resources: lisajvogt.com/
Become a Premium Video Member today here: lisajvogt.com/glass-fusing-wi...

Пікірлер: 15

@3PairDesigns 2 ай бұрын

As always, you are so fun Lisa, thank you so much for sharing! Excellent inspiration. I've never tried weaving but have always wanted to. You have really helped demystify it! ❣

@bethsherbert7862 4 күн бұрын

Awesome video! Thank you!! ❤

@vrothery50 2 ай бұрын

I have to get a mold like that-very cool! TFS!

@carolyncross6501 2 ай бұрын

Thank you Lisa!!!

@AnnetteRintelmann 2 ай бұрын

THAT IS COOL!!!!!!!!!!!!!!!!!!!!!!

@stephencouitt3831 2 ай бұрын

Definitely need to try this.

@gillcottam8152 2 ай бұрын

If you cant get the mould i used fat chalk ,very cheep and i measured set distances❤

@roseannegibson3343 2 ай бұрын

Awesome

@sherrirowan5049 16 күн бұрын

Hi Lisa. What brand is your weave mold. I’d like one like that ❤

@1wanderingbob 2 ай бұрын

Lisa what was the specific mold you used for making the weave parts, it is nicer then the ones we have

@LisaVogtglassartist 2 ай бұрын

www.fireliteforms.com/product/5303 Here's the mold I use!

@erinconrad1335 2 ай бұрын

You said the same temps for both the slump temp and the tack fuse - 1365. That seems quite high for a slump temp, but right for a tack. Is that an error? (I was just thinking this afternoon about trying a weave!)

@LisaVogtglassartist Ай бұрын

Just to clarify, slump temps for COE 96 is 1265 and tack is 1365 :). Slump temps are just hot enough to cause the glass to "sag" and conform to the mold. For tack fusing, 1365 is hot enough to get the glass to stick together and give you shiny edge quality. I hope this helps!