Making lemonade out of lemons: fused glass scrap melts using peacock blue disasters.

Рет қаралды 31,428

Jamaison Schuler, Fused Glass Artist

3 жыл бұрын

Glass used: Bullseye peacock blue (1176) and Tekta
Stainless steel formers, 1/8" fiber paper strips and ceramic bottomless bowl mold from Laurie Spray (bonnydoonfusedglasstools.com)
As an Amazon Affiliate I earn for qualified purchases.
Frit piston: search Google -- lots of retailers sell this model, and there are crafty types who also make and sell their own. Here's the specific one I have: amzn.to/3l5BcXH
Frit sifter set: again, many retailers sell this. Or get clever and make your own! amzn.to/3FHot5l
To figure out the amount of glass needed, first calculate the volume of the glass you are trying to achieve such as the diameter of the circle and 6 mm final thickness. There are plenty of online calculators for this, but I used: www.calculator.net/volume-cal...
Then I took the volume and plugged it in here: fusedglass.org/tools/pot-drop...
First fuse firing schedule:
400-1225-60
500-1480-30
9999-900-120
100-700-0
Second firing to add clear powder and more glass around the edges:
300-1225-30
500-1480-30
9999-900-120
100-700-0
Slump schedule:
250-1225-45
9999-900-120
100-600-0

Пікірлер: 75

@joanjetson55 9 ай бұрын

I like the end result, including the bubbles! It has the overall appearance of shamrocks somehow, and it's very appealing; not at all a disaster in my view. The bonus piece is also lovely, and cleaning the pieces between firings to avoid spalling is a much appreciated suggestion. Thank you!

@unarobinson7392 3 жыл бұрын

I add a layer of shelf paper around the sides over the fibre and get no spikes.

@jenniferfragomeni8064 3 жыл бұрын

I LOVE scrap melts! Instead of ramping at full speed to the process temp, I usually ramp up 800 dph. Works like charm!

@carolking8891 2 жыл бұрын

I love the bubbles.

@user-os7ck8rc7e 10 ай бұрын

I love your videos. I have been on a glass fusing break for 6 years and only working copper foil glass. So happy to be back at fusing. Love all my Laurie Spray pot melts and steel rings. Felt rusty so your videos are helping me. Lots of "OH RIGHT!" coming out of me, lol. Thank you

@JamaisonSchuler 10 ай бұрын

We’ll stay tuned… I have another project underway now! Lord knows when I’ll finally edit and upload though… 😂

@acprive 3 жыл бұрын

Funny, people get an idea of what someone looks like from their voice. You look nothing like I had imagined, in a good way:) I made one of these years ago and also had the bubbles. I brought it to another glass artist and she asked me how long I held at full fuse. When I told her 30 minutes she immediately said it should have been 60 minutes. I honestly haven’t made one since. I was thinking yesterday I need to use up a lot of my scraps and I dug out three of my rings. Thanks for the videos and happy new year.

@pennyfoster9392 2 жыл бұрын

Great video and great use of scraps. The bowl is beautiful. I use a lower and slower bubble squeeze. you may try something like this 400 to 1125 then ramp at 50 (yes 50) to 1275. then finish your schedule. this gives the glass a long time to settle and get bubbles out. The only drawback is it add 3 hours to your firing. I use this on everything bigger than a jewelry piece.

@JamaisonSchuler 2 жыл бұрын

I’ve been doing something very similar, going to 1100, hold, then 50dph until 1250. I do like that schedule!

@jimscott3060 2 жыл бұрын

Recycle is the way, double the joy…. Pleased to have your ease and humility in my learning - great day

@maryshevlin7667 3 жыл бұрын

For the dimples/bubbles, use a dremel with a ball bit to break them open (or press a sharp pointy tool into them to break open.) Fill with a clear chip of glass the full fuse.

@vivagypsy 3 жыл бұрын

Exactly...That is what Laurie told me to do also and it really works!!!

@birgittelutfy8733 2 жыл бұрын

I agree, I would have done that after the first firing

@lindacondray7918 3 жыл бұрын

Make your own frit wo metal flakes in it. USE CARE WITH HOT GLASS! In small kiln heat a pile of scrap to 1500°F. Using long vitrograph pliers and leather gloves, safely grab molten glass and drop in steel bucket of water. Pour off water and dry. Sort w frit sorter. Advantage of this method is no metal fragments in the frit. I use frit as froth on edges of floral vases and filler between “coral” style bowls.

@JamaisonSchuler 3 жыл бұрын

I’ve seen this demonstrated before... not sure I’m brave enough! 😂

@stormyhaverkate6573 3 жыл бұрын

So happy to have found you! Thanks for the cool info on fused glass!

@madonart 2 жыл бұрын

These two pieces are beautiful.

@philcox2845 3 жыл бұрын

Love this one. I will have to try that at some point. Thank you for showing this and the process

@pattimessenger6214 2 жыл бұрын

I love both projects! And I love that peacock blue!

@elt3369 Жыл бұрын

This is beautiful with every little bubble the extra characters 🙏🏿😎💥🤓🤩

@madonart 2 жыл бұрын

Thank you. I am very interested in learning about working with glass.

@wlgleason Жыл бұрын

Good videos. Thanks. I used to use the black iron frit maker that you have but switched to using an old electric blender with a thick heavy duty glass blender jar. You can get them cheap at secondhand stores. Works great. You need to wear an adequate face mask while working. After crushing the glass and before removing the lid, I suck the glass dust out of the jar using a shop vac through the small top opening. Then I use the sifters as you do. You can make a lot of frit in no time.

@kaymcconnell4221 2 жыл бұрын

I love this bowl. I do wish that you had shown you 'carefully removed the glass' from the SS former after the second firing. Thanks for this wonderful video.

@mariannepotter8159 8 ай бұрын

Beautiful projects! I really enjoy the way you provide great explanations. Very helpful and appreciated.

@pamelamccann2299 3 жыл бұрын

You’re a cutie pie! Thanks for sharing what you’re doing. it’s always nice to have some new blood and fresh ideas.

@lynnmassey-davis7879 2 жыл бұрын

Thank you, great project

@elt3369 Жыл бұрын

Both projects are gorgeous this is my first time watching your videos. Blessings 🙏🏿

@jannarichard3222 3 жыл бұрын

I love your videos. There is always something new to learn! And today I learned that I have mold storage envy!! Great Idea on the bakers racks!

@JamaisonSchuler 3 жыл бұрын

I’m not sure how I’d survive without those!!! Look for used ones locally. They hold a crazy amount of molds or glass works-in-progress!

@kartermarcus3565 2 жыл бұрын

you probably dont give a damn but does any of you know of a way to get back into an instagram account? I somehow forgot my account password. I love any assistance you can offer me!

@andymark2806 2 жыл бұрын

@Karter Marcus Instablaster =)

@kartermarcus3565 2 жыл бұрын

@Andy Mark thanks so much for your reply. I found the site thru google and im in the hacking process now. Seems to take a while so I will reply here later with my results.

@kartermarcus3565 2 жыл бұрын

@Andy Mark it worked and I actually got access to my account again. Im so happy! Thank you so much you saved my account :D

@vickypage8653 3 жыл бұрын

Love your videos! I learn something new every time and really look forward to seeing more!

@JamaisonSchuler 3 жыл бұрын

Thank you! I’m learning too!

@artisticexchangepodcast 3 жыл бұрын

Enjoy your videos! Thaks and keep them coming!

@3PairDesigns 3 жыл бұрын

Jamaison, good to see your handsome face! I love your scrap adventures, I usually learn things I didn't know, like those steel molds throw off what looked like carbon, who knew? I may have heard it in the past but didn't realize it. I still think your processes are good and one thing I have learned in a decade of doing fusing and learning along the way, is that sometimes "lower and slower" can get the job done. However, having said and done that, it has NOT always been the answer. I was going to say that the information that acprive (below) was also where I was leaning. A longer old time may have allowed the bubbles to fully surface and "equalize" themselves. Regardless, I really did like BOTH videos and I enjoy your sense of adventure. Thanks as always, and Happy New Year! 😉👍

@suzieguirsch1065 3 жыл бұрын

I just love your videos.! I'm very new to fusing and your videos have helped me so much.. You always have great information

@richardh5983 Жыл бұрын

I'm new to fusing and love your video's! Thank you so much for teaching, and sharing your various techniques that you use. Look forward to more, and Thank you!

@suzodell7996 Жыл бұрын

Newbie here… thanks for the insights.. beautiful pieces 😍

@jeannerehfuss4648 3 жыл бұрын

Hi Jamaison! Love your videos! I have been inspired by all of them! I think that the large size bubbles would have been reduced by slowing down in the bubble squeeze zone. If I am doing something that is likely to trap air I slow my schedule down starting at 1100 degrees. I then go 100 to 1175, H20; 45 to 1225, H30. As the glass starts melting a longer bubble squeeze will give the air more time to exit the piece. I think that on the second firing with the long hold at the top temp it allowed the bubbles to move to the surface more, causing some to break open.

@JamaisonSchuler 3 жыл бұрын

Very helpful. Thank you!!!

@handslary7459 3 жыл бұрын

Your initial fuse probably had a bit of shelf release on the bottom of each plate. Before turning to frit you should have cold worked a bit to grind off any release agent. I'm thinking that your bubbles were a result of primer contamination.

@lesselavie7675 3 жыл бұрын

Pretty!

@nancymckenzie3258 3 жыл бұрын

Love your videos and it’s a plus getting to put a face with your voice. I only have a MWK, but still get lots of tips from your videos!

@patriciapeterson2820 3 жыл бұрын

Beautiful ❣️

@rutesabino3477 2 жыл бұрын

Obrigada, por compartilhar, sua sabedoria.

@clkahn 3 жыл бұрын

Hi J - I would have done a bubble squeeze the second firing holding for 1:30 at 1225.

@JamaisonSchuler 3 жыл бұрын

Thanks for that... that’s where my head is too, especially since I could see some of those bubbles after the first firing.

@maryshevlin7667 3 жыл бұрын

I do 400 ph to 1200 and hold 30, then 300 ph up to 1500 and hold for 40 minutes. I don't have bubbles.

@JamaisonSchuler 3 жыл бұрын

Thanks!!!

@heatherrevezzo 2 жыл бұрын

Great video, I'm glad I stumbled onto this! Also, love that you put a link up for calculations. And also, frit piston?!?! I definitely need one o those! Thinking about your bubble issue with the second firing, maybe you needed to hold the 1480 at longer to squeeze more of the bubbles out? And yes maybe the slower/lower temp ramp contributed. Also what if you flipped the piece for the slump? Maybe that would hide the bubbles and reverse their trajectory, so they were more in the middle of the piece instead of appearing like pitting on the surface. Overall thought I think it's a great finished piece and love how you recycled your scrap projects. I have subscribed to your page, and looking forward to watching more. I will definitely be trying this!

@lynnmassey-davis7879 2 жыл бұрын

Great smile !

@lynnmassey-davis7879 2 жыл бұрын

Thank you 👍😁

@gbleimeyer3659 3 жыл бұрын

The "flaws" we see are really the hand of the artist. Thanks for another great video.

@lynnmassey-davis7879 2 жыл бұрын

You look great and have a wonderful smile

@dorothyclark1989 3 жыл бұрын

no idea on the bubbles. I have been doing glass for about the same amount of time and boy, I wish I had the set up you have. I do all my fires at 300 degree increments so really have no idea on why you would have got more bubbles. I do like this piece. Can you do a video on how you use your frit maker? I would appreciate that. Happy New Year.

@susanbartley8741 9 ай бұрын

We call this a saucer melt nice job

@kallbabs 3 жыл бұрын

When you top a glass with a textured glass, do you put the texture side down or up? If it’s down, wouldn’t it trap more bubbles? Also, use a full fire?

@JamaisonSchuler 3 жыл бұрын

I can’t find the source offhand, but I’ve read that firing Bullseye tekta with the texture side down and using a good bubble squeeze will reduce bubbles. It seems counterintuitive, and I wish I could find the source!

@rutesabino3477 2 жыл бұрын

Amei

@aomanchutube 3 жыл бұрын

Do you know if you mix powder alumina and mix it with borosilicate frit, does the end result after firing get lower CTE? I want to bond alumina, but my current glass is crazing.

@JamaisonSchuler 3 жыл бұрын

Gosh, I have no idea!

@aomanchutube 3 жыл бұрын

@@JamaisonSchuler I'm learning technical glass for industrial use. Watching videos of various types related to frit and paste glass. Paste glass is awesome by the way. I'm going to ball mill some glass and alumina soon and see if the mix crazes less.

@cindydouthit8029 3 жыл бұрын

How often can you reuse that fiber ring?

@JamaisonSchuler 3 жыл бұрын

I’ve used it twice and it’s ready for a third firing. May depend on how careful you are with it? I’m hoping for as many times as possible!

@joanieb45 3 жыл бұрын

You’re adorable!

@jenmather4112 3 жыл бұрын

How do you calculate how much glass you need? Thanks.

@JamaisonSchuler 3 жыл бұрын

I added those notes and web links in the video description

@elinorbell3140 Жыл бұрын

Love these ideas!! How do you calculate how much glass to use?

@JamaisonSchuler Жыл бұрын

It’s mostly just a guessing game for me. I like to live dangerously 😉

@elinorbell3140 Жыл бұрын

@@JamaisonSchuler oh, I wondered because you said in the video that you had calculated the amount of glass needed...

@JamaisonSchuler Жыл бұрын

@@elinorbell3140 oh, yes, there is a Calculator, check the video notes, and there is some information in there on how to do that. But at this point, I’m just guessing every time I do this. But if you want to be formal about it, there is a process and you can find it in my video notes.

@elinorbell3140 Жыл бұрын

@@JamaisonSchuler thank you 😊