i decided to do a series of videos about tips around edge retention. I will try to keep the videos a bit shorter and concentrate on smaller pieces of each tip. this one has to do with expectations about edge retention, what will dull your edge and what will just wreck it. caltoncutlery.com

Пікірлер: 24
@1963BillyB
@1963BillyB 2 ай бұрын
Best "real" words reflecting common sense and experience...excellent...thank you
@joecalton1449
@joecalton1449 2 ай бұрын
Glad you enjoyed it!
@S.Vallieres
@S.Vallieres Ай бұрын
Excellent video that puts edge retention expectations in perspective. Thumbs up!
@joecalton1449
@joecalton1449 Ай бұрын
thanks!
@adamboone6864
@adamboone6864 2 ай бұрын
Your videos on sharpening are awesome. Learned a lot. Youve given me confidence to start making my own knife.
@joecalton1449
@joecalton1449 2 ай бұрын
that is very cool! I hope your knife turns out good!
@ericasedc
@ericasedc 2 ай бұрын
Excited for this one!
@joecalton1449
@joecalton1449 2 ай бұрын
I hope you enjoy them :}
@muhammedk470
@muhammedk470 2 ай бұрын
After long, a knife sharpening video
@joecalton1449
@joecalton1449 2 ай бұрын
yes, it has been a little while. but there are quite a few coming for the next couple months at least :}
@muhammedk470
@muhammedk470 2 ай бұрын
​@@joecalton1449Looking forward to them. Thanks for taking the time to share your experiences
@JohnDoe-zb7dz
@JohnDoe-zb7dz 2 ай бұрын
Always nice to get a JC fix. Looking forward to more. Thanks for sharing Joe.
@joecalton1449
@joecalton1449 2 ай бұрын
Thanks 👍
@DoingMoreKustoms
@DoingMoreKustoms 2 ай бұрын
Great tips and video. Big thumbs up.
@joecalton1449
@joecalton1449 2 ай бұрын
Thanks for watching!
@ChuckinSteel
@ChuckinSteel 2 ай бұрын
Excellent video Joe. 👊
@joecalton1449
@joecalton1449 2 ай бұрын
thanks!!
@Nebulax123
@Nebulax123 Ай бұрын
That is why I have two hatchets one that is mine and has a polished razor edge and one I loan which has a nice edge at least when I loan it. lol
@joecalton1449
@joecalton1449 Ай бұрын
and when someone asks you if they can borrow a knife, before you say yes, you ask "what for" :}
@Casiomidi1
@Casiomidi1 2 ай бұрын
Is it preferable to stop sharpening/honing just short of attaining extreme razor sharpness as the edge will be microscopically thicker and will hold up better. In the shaving world, DE Feather blades are reputed to be the sharpest but dull after just one maybe two shaves at best
@joecalton1449
@joecalton1449 2 ай бұрын
i have heard of folks doing that. my biggest question is how do you know that you are stopping just short? how far short would you have to stop, and is that repeatable? and is that the way that you like to work? i like a sharp knife, so I sharpen to a sharp edge, then touch it up as needed until its time for a complete new edge, then sharpen and repeat.
@rickwhitson2804
@rickwhitson2804 Ай бұрын
Just for curiosity what state are you in???
@joecalton1449
@joecalton1449 Ай бұрын
Wyoming
@rickwhitson2804
@rickwhitson2804 Ай бұрын
@@joecalton1449 Great place to live. It's one of my favorites
knife edge retention tips 2 corrosion
8:51
Joe Calton
Рет қаралды 548
knife edge retention tips 11 knife skills
9:06
Joe Calton
Рет қаралды 269
⬅️🤔➡️
00:31
Celine Dept
Рет қаралды 50 МЛН
ROCK PAPER SCISSOR! (55 MLN SUBS!) feat @PANDAGIRLOFFICIAL #shorts
00:31
LOW VS HIGH ANGLE EDGES EDGE RETENTION
18:56
Neeves Knives
Рет қаралды 23 М.
knife edge retention tips 3 sharpening isnt a bad thing
9:31
Joe Calton
Рет қаралды 1 М.
Trip to Red Hill Cutlery!
10:52
Ted Hart
Рет қаралды 1 М.
There is no shortage of ways to sharpen serrations, I have tried many. Here is my favorite.
13:36
Alexandria Knife Sharpening & Laser Engraving
Рет қаралды 72 М.
knife edge retention tips 6 glazed or dirty stones
14:42
Joe Calton
Рет қаралды 695
knife edge retention tips 4 the burr
8:22
Joe Calton
Рет қаралды 1,4 М.
knife edge rentention tips 5 destressing the old edge
11:49
1095 high carbon steel pocketknife daily maintenance
17:43
Joe Calton
Рет қаралды 1,1 М.