No Gap ! 6G TIG Welding Technique | Stainless Steel

No Gap ! 6G TIG Welding Technique | Stainless Steel | Sch.10 !

Рет қаралды 105,125

2 жыл бұрын

6G TIG welding technique stainless steel sch.10 No gap!
TIG welding stainless steel can feel like a horrific nightmare when you’re starting out.
The main reason people have so much trouble with it is that they take shortcuts. You cannot take shortcuts with stainless steel. It will always rebound back at you with ugly welds and often a ruined project.
Follow the right steps, and the quality of your next TIG welding job will improve dramatically.
Lots of KZfaq welding gurus will show you easy welding in 5G roll out with perfect outcome. The reality is completely opposite in the field. This video is made to help out people who are struggling with stainless, passing the job test, or just getting better in their game.
#tig #tigwelding6G #stainless
None of these videos are recorded in a fancy shop surrounded by sponsorship banners!
All of my videos are recorded at working sites in various locations and different welding positions.
90% of my welding projects in videos are x-rayed, and if you like to see hands-on projects, welcome!
If you liked this video please give it a thumbs up, share it, subscribe and click the bell.
It doesn’t cost you anything but massively helps my KZfaq channel. Thank you.
Support this channel with 🔔 Subscribe and 👍 Like!
/ x3mtig

Пікірлер: 93

@X3MTIG 2 жыл бұрын

Subtitles option available!

@jamessmith5905 Жыл бұрын

Where

@danieleriquez5769 5 ай бұрын

@@jamessmith5905😅😅

@danieleriquez5769 5 ай бұрын

@@jamessmith5905😅😅

@danieleriquez5769 5 ай бұрын

@@jamessmith5905😅😅

@mikewoodford9003 26 күн бұрын

In the CC box, toggle it to English captions or whatever language you like. @@jamessmith5905

@joshdescant3250 9 күн бұрын

sch 10 stainless is my favorite welds to make...quick easy and clean welding...love it

@SeldomFales 2 ай бұрын

You’ve asked a very good question that most cup-walkers can’t answer better than the this welder. I’m very old school from when “freehand or finger-walking” tig ruled the day and cup-walking was very new. There is a visual sign of full penetration with tig SS but using the freehand technique. The visual sign is being able to see what we called the “fusion line or the penetration line” down the center of the SS root/1st pass. This is not seen cup-walking!

@colbywedgworth9676 Ай бұрын

I see that cup walking also. You should see it regardless or your root is probably sucked back or non consumed edges.

@Smurf51766 6 күн бұрын

Most definitely can do it walking the cup. Maybe not as easy but nothing in welding is impossible

@JohnDoe-yh6sn 2 жыл бұрын

Great as always!✊One can indeed learn a lot from you! Thank you for spreading your knowledge so unselfishly! Rarely good content! 💪🏻

@X3MTIG 2 жыл бұрын

Thank you for your comment 🙏

@dariom5050 2 жыл бұрын

Odlicno zavareno!! Ovo je fakat tesko i hvala ti puno na detaljnoj deskripciji! 👏🏻👍🏻

@X3MTIG 2 жыл бұрын

Thanks buddy 👍

@johnmoriarty6158 Жыл бұрын

You make that puddle move seemingly effortless. Thank you for sharing.

@marijoivicic7380 2 жыл бұрын

Svaka čast majstore

@tomislavkojadin3657 2 жыл бұрын

Thank you for posting! 👏👏

@X3MTIG 2 жыл бұрын

Thanks bud!

@anks4343 2 жыл бұрын

Amazing video and great skills! 👍🏻🔥🔥

@X3MTIG 2 жыл бұрын

Thank you very much!

@bit4ever823 2 жыл бұрын

Nice video 👍

@kaumkau9065 11 ай бұрын

Отличная сварка брат! Спасибо за видео!

@robertas861 2 жыл бұрын

Thank you for posting this one!🔥🙌🏻 You have amazing and quality content, incredible skills , thanks for the subtitles! ☺️

@X3MTIG 2 жыл бұрын

My pleasure 😊

@luismoya6268 5 ай бұрын

Excellent master

@kerryodjugo5464 Жыл бұрын

You are the genius

@absteelmaster3939 Жыл бұрын

Nice man

@laurenceaoun6191 2 жыл бұрын

Very good tecnik. That's good idea. And the welder is intelligent 👌

@X3MTIG 2 жыл бұрын

Thank you my friend 🙏

@ryanmcguinness7898 Жыл бұрын

What amps for the cap or did you leave it on 90

@micmike Жыл бұрын

Nice demo of field conditions... be the puddle!

@skullbeard1339 Жыл бұрын

Perfectly! When welding the root, did you control that the bath was about 7 mm? the root is even on the ceiling ( in the position above the head ) came out well! The bath is mixed and the additive drops?! Thank you for your work!!!

@_trader123 10 ай бұрын

Sem dúvidas, otimo profissional, ja tentou fazer a capa com menos material, tipo movimenotos mais longos e pouca adicao de vareta....só uma dica ..

@wtfatc4556 2 жыл бұрын

Really nice root there!

@johnhannigan7311 8 ай бұрын

Nice job man 👌What amps did u run the cap at

@ryanmcguinness7898 Жыл бұрын

What amps do you suggest for 5g

@yusni5 Жыл бұрын

Excelente trabajo 👍 saludos

@X3MTIG Жыл бұрын

Thank you! 😊

@user-so1gp1mp3i 5 ай бұрын

Yeah thats no doubt a skilled welder

@jorginflowers3026 Жыл бұрын

Perfecto 👌

@travisjones9508 2 жыл бұрын

Whenever I test I like doing the uncomfortable side first. That way I can make it or break it. Repair or let them run me off

@X3MTIG 2 жыл бұрын

Thanks for your comment bud! I do that as well, lol!

@duraebroughton8015 Жыл бұрын

wats the temp on the root full and cap

@Qwer0121 2 жыл бұрын

Nice welding bro

@X3MTIG 2 жыл бұрын

Thanks bud!

@gerrylimmy Жыл бұрын

Hi.Mr. Can You explain me for what the flowing argon injected into inside Mr?

@X3MTIG Жыл бұрын

Thanks for your comment bud. Argon was set to 25-30 Lpm

@marioochoa4298 Жыл бұрын

I have issues on the bottom sometimes with suckback any tips to help correct this? Thanks great content and showing some of your knowledge

@X3MTIG Жыл бұрын

try with the heavier root at the bottom, it might help on hot pass!

@mikewelder7014 2 жыл бұрын

This video is pure perfection!!! 👍🙌🏻Incredible skills!!! This is so hard to weld, and especially considering the fact there is no gap!! What size of welding rod did you use brother? Thank you! 😊🤝

@X3MTIG 2 жыл бұрын

Thank you for your comment brother. I used 3/32 filler rod.

@aswishersweets Жыл бұрын

Could you do this with out the control

@lawinanakdigat9594 2 жыл бұрын

Failed how about inside if got rt?

@smartybjp Жыл бұрын

Is it possible to make back-bead at overhead position with no-gap condition? like that?

@X3MTIG Жыл бұрын

Hey bud, thanks for your question . Good question btw.👍 Honestly I’ve never tried that technique on the pipe. Usually that technique is used when heat input is controlled and mostly on thin sheet plates. I don’t think that would work with no-gap joint as you need continuous heat input to form that root inside. Thanks once again, you give me something to think about 💪👍

@tjaydagreat 2 жыл бұрын

Nice weld man. Ive never welded stainless with no gap. Your root is still meaty with no gap. Im gonna try this when I get on a job and have time to fuck around on lunch.

@X3MTIG Жыл бұрын

Thanks for your comment bud! 😊

@kalleklp7291 5 ай бұрын

Well done! Yeah, out there you got to deal with all kinds of crap and never expect the material to be perfect. TIG welding is my favorite. It's so nice and clean without sparks and metal drops flying around like stick welding does.

@X3MTIG 5 ай бұрын

Well said!

@dylanwhite3841 Жыл бұрын

Is there a way of telling if your getting good penetration on the root while doing it? And what are your thoughts on doing it in one pass? Great work by the way!

@X3MTIG Жыл бұрын

Thanks bud, you could tell by the puddle , and mostly experience. One pass, only on thinner wall.

@timothyhendershott9333 2 жыл бұрын

Thanks for posting the video. It could only be improved by adding a audio commentary. Thanks again.

@X3MTIG 2 жыл бұрын

Thanks for your comment bud! Maybe you are right, but english is my second language, so I choose not to use audio commentary!

@shrinathpujari6092 6 ай бұрын

How much current

@eliaslourencosantos5122 Жыл бұрын

Boa noite, soldei tubulações de inox, para área alimentícia, farmacêuticas, tem que ser um soldador que gosta que esta fazendo, SOLDAR é uma arte, o artista tem que ter amor naquilo que faz, sou professor na área de solda, conheço todos os tipos de possesso na soldagem, todos os tipos de materiais, gosto do que faço, e gosto de ver vídeos soldadores SOLDANDO em áreas abertas ou fechadas,SOLDAR é uma ARTE.

@X3MTIG Жыл бұрын

Very well said my friend 👍

@OG______ 2 жыл бұрын

Could show how to do it without the bevel ? (but still use wire)

@OG______ 2 жыл бұрын

love your videos btw 🙌 I think your channel is relly underrated.

@X3MTIG 2 жыл бұрын

Thanks for your comment and support bud! On schedule, 10 pipes without a bevel is a little bit difficult as you won't get much penetration, especially on the overhead part, and I don't think that anyone will have such a challenge in the field. If you do! You can refuse that, and ask your fitters to fix that or give you a gap. You can do it in the rollout, but only for entertainment purposes. On schedule 5 it's a different story, you can perform welding without gap and bevel. As soon as I got my hands on schedule 5 I will make a video about it.

@sierraturan5115 2 жыл бұрын

What size tungsten?

@X3MTIG 2 жыл бұрын

Tungsten 1/8

@thrustprop67 Жыл бұрын

what local you from ,,, very nice work

@X3MTIG Жыл бұрын

With 488 atm

@user-vo4hl2gd3j 2 жыл бұрын

👍👍👍👍

@hectorleon9940 2 жыл бұрын

Quantos amperes no enchimento ?

@X3MTIG 2 жыл бұрын

Hey bud, around 130 amps

@time4497 Жыл бұрын

👍

@user-pp3nf1td7o Жыл бұрын

👍👏👍

@CP-jt6bw 7 ай бұрын

QC wouldn't let that happen. The heat input is too high the travel speeds too slow and the procedure calls for a gap. But I'll probably still give this a try next time I'm in a welding booth

@thrustprop67 Жыл бұрын

you mean 488 edmonton don't know what atm means ,,, I am 527 but started with 488 40 years ago

@olaakin6621 Жыл бұрын

@8:50 your pipe got bursted bcos of delay and too much heat at a spot..

@X3MTIG Жыл бұрын

That’s right.

@InitiallyJB Жыл бұрын

Too much pressure of argon was inside the pipe. Remember you have to let the purge bleed out as well. Even though you had 4 air holes to vent you need to adjust your argon flow rate to maybe 10-20lbs of pressure less and more flow on your tig rig. Then for the cap you can turn argon back up and suck back your root in that’s if you weld it all hot. If you let it cool then you can keep flow at the vent flow

@user-yj3io1pu8p 10 ай бұрын

I.wamt practical to this welding. Iam a gyas welder

@brianbeaubien7371 Жыл бұрын

Why no talking?

@X3MTIG Жыл бұрын

In Old videos I didn’t use voice over.

@eduardogonzales3212 Жыл бұрын

Muy feo se ve el video al estaraoldando

@mikewelder7014 Жыл бұрын

You have to understand that is not easy to record the welding process, especially if you consider the fact that this guy is a field welder. He records his videos while working on various job sites, unlike many other video creators who are recording their videos in their own shop and have all the time it takes to record, plus they have also lots of money from KZfaq to provide them with the best possible equipment! This guys is just a normal welder who works and struggles just like the rest of us and gives his best to teach people!

@Ashford_welds 7 ай бұрын

@@mikewelder7014so true this is real talk. He brings is as raw and real as possible, its real life scenarios and real life jobsites. He still lucky, some plants I worked at you can't even use your phone🤦🏿🤦🏿. Much yet to record a whole welding process. You also must have a good friend to record for you as well cause not everyone is willing to just record you at any given time.

@liamjenkins82 Жыл бұрын

So with Sched 10, it's fairly normal for it to have a dark colouring on the cap. I've been doing some Sched 10 full purge for work. All my caps are a very dark purple. Never the nice shiny silver!

@X3MTIG Жыл бұрын

Try to wait for your pipe to cool down before putting cover pass.

@liamjenkins82 Жыл бұрын

@@X3MTIG thanks. I've been doing that. They came out a little better. Trying to get myself in to pressure welding in australia after 20 years of fabricating. Videos are helping lots. Thanks

@user-kh6zp2bj5s 10 ай бұрын

Do you keep it purging through all the passes? I noticed it too with sched10...I also need to let it cool more... been doing the same at work, 4" sch10 stainless...316L though but no gap and full purge. Low pressure for ozone plant